... glass expansion curve ( Fig . 53 ) so that stress - free seals can be produced by matching glasses with metals of equal total expansion at the annealing temperature only . A perfect matching ... GLASS - TO - METAL SEALS Glass-to-metal seals.
... glass expansion curve ( Fig . 53 ) so that stress - free seals can be produced by matching glasses with metals of equal total expansion at the annealing temperature only . A perfect matching ... GLASS - TO - METAL SEALS Glass-to-metal seals.
Σελίδα 124
... glass is still considerable . A lengthy anneal of glass at a fixed temperature followed by a relatively rapid subsequent cooling can alter the virtual temperature from which internal stress starts building - up as well as the resulting ...
... glass is still considerable . A lengthy anneal of glass at a fixed temperature followed by a relatively rapid subsequent cooling can alter the virtual temperature from which internal stress starts building - up as well as the resulting ...
Σελίδα 126
... glass , and the outer radius of the glass . It is interesting to note that in seals of a thick glass tube on a thin - walled metal tube the stresses are low since , as should be expected , the tube is then weak and deforms under the ...
... glass , and the outer radius of the glass . It is interesting to note that in seals of a thick glass tube on a thin - walled metal tube the stresses are low since , as should be expected , the tube is then weak and deforms under the ...
Περιεχόμενα
GENERAL CONDITIONS FOR WETTING AND FOR ADHESION | 3 |
MOLECULAR FORCES | 13 |
RHEOLOGY OF ADHESIVES | 52 |
Πνευματικά δικαιώματα | |
21 άλλες ενότητες δεν εμφανίζονται
Άλλες εκδόσεις - Προβολή όλων
Συχνά εμφανιζόμενοι όροι και φράσεις
abrasive acetate acid addition adherends adhesive layer alkali amylopectin amylose animal glue applied asphaltic bitumen bitumen bond cellulose cement CH₂ Chem chemical chlorinated clay coating colloidal composition compounds compressive concentration corrugated deformation depends dextrines dilute dried drying elastic factor fiber fillers film formaldehyde glass glue solution glued groups hardening heat humidity increase industry kg/cm² laminated lap joints latex lbs/sq liquid load manufacture materials metal mixture modulus moisture molecular weight molecules Na,O Na₂O Neoprene obtained oxide paper particles penetration phenol plastic plate plywood polar polymer polymerisation polyvinyl polyvinyl acetate properties ratio react reaction resorcinol rheological shear strength shear stress sheet silicate solution sodium silicate sodium silicate adhesives solid soluble solvent starch structure sulphur surface TABLE tackiness temperature tensile strength tension thermoplastic thickness thixotropy urea viscosity vulcanization water resistance wetting wood