Adhesion and Adhesives, Τόμος 1Elsevier, 1951 |
Αναζήτηση στο βιβλίο
Αποτελέσματα 1 - 3 από τα 85.
Σελίδα 73
... thickness of the adhesive layer . MCBAIN formulated this effect as follows : " The thinner the adhesive layer , the stronger the joint . The effect of thickness is not appreciable with thick films , but rapidly increases when the ...
... thickness of the adhesive layer . MCBAIN formulated this effect as follows : " The thinner the adhesive layer , the stronger the joint . The effect of thickness is not appreciable with thick films , but rapidly increases when the ...
Σελίδα 75
... Thickness of Glue microns Fig . 30. Joint shear strength of resin glue in relation to thickness of glue film . J. W. MAXWELL , Trans . Am . Soc . Mech . Engrs , 67 ( 1945 ) . a point where the glue film thickness approaches 80 mi- crons ...
... Thickness of Glue microns Fig . 30. Joint shear strength of resin glue in relation to thickness of glue film . J. W. MAXWELL , Trans . Am . Soc . Mech . Engrs , 67 ( 1945 ) . a point where the glue film thickness approaches 80 mi- crons ...
Σελίδα 112
... thickness of the adhesive of glued and soldered joints is increased 23-27 ( Fig . 48 ) . The dependence of tensile strength on thickness is , however , complicated by other factors such as the development of residual strains which are ...
... thickness of the adhesive of glued and soldered joints is increased 23-27 ( Fig . 48 ) . The dependence of tensile strength on thickness is , however , complicated by other factors such as the development of residual strains which are ...
Περιεχόμενα
GENERAL CONDITIONS FOR WETTING AND FOR ADHESION | 3 |
MOLECULAR FORCES | 13 |
RHEOLOGY OF ADHESIVES | 52 |
Πνευματικά δικαιώματα | |
21 άλλες ενότητες δεν εμφανίζονται
Άλλες εκδόσεις - Προβολή όλων
Συχνά εμφανιζόμενοι όροι και φράσεις
abrasive acetate acid addition adherends adhesive layer alkali amylopectin amylose animal glue applied asphaltic bitumen bitumen bond cellulose cement CH₂ Chem chemical chlorinated clay coating colloidal composition compounds compressive concentration corrugated deformation depends dextrines dilute dried drying elastic factor fiber fillers film formaldehyde glass glue solution glued groups hardening heat humidity increase industry kg/cm² laminated lap joints latex lbs/sq liquid load manufacture materials metal mixture modulus moisture molecular weight molecules Na,O Na₂O Neoprene obtained oxide paper particles penetration phenol plastic plate plywood polar polymer polymerisation polyvinyl polyvinyl acetate properties ratio react reaction resorcinol rheological shear strength shear stress sheet silicate solution sodium silicate sodium silicate adhesives solid soluble solvent starch structure sulphur surface TABLE tackiness temperature tensile strength tension thermoplastic thickness thixotropy urea viscosity vulcanization water resistance wetting wood